Cold Rolled 420J2 Stainless Steel Strips ASTM A240 3Cr13 SS Strips / Stainless Steel Roll
420 J2 is a general purpose stainless steel containing medium quantity of carbon. It has good corrosion resistance qualities in mild atmosphere, domestic and industrial environments. It is resistant to ammonia, blood, carbonic acid, crude oil, detergent solutions, dilute nitric acid, fresh water, food acids, many petroleum products, steam and vinegar, etc. It has good strength and reasonable impact resistant properties in both hardened and tempered conditions as compared to 440 grades.
It is also called Surgical Steel, because it is being used in production of Surgical instruments on large scale around the world, due to its good corrosion resistant and easily machining qualities. It is also being used in cutting tools like; Knifes, Daggers, Swords, Haircutting Scissors and Domestic Scissors. It’s grinding is easy and it produces a fine, vivid and smooth polished surface.
420 steel, due to its excellent harden-ability, it is capable of getting hardened up to 56 HRC Rockwell or higher depending upon carbon contents / composition. Small sections can be air or gas cooled and larger sections should be oil quenched for maximum hardness.
Heat Treatment Sub-Critical Annealing:
Heat uniformly to 730 °C - 790 °C and hold until temperature is uniform throughout the section.
-Soak as required, cool in air.
Heat uniformly to 840 °C - 900 °C and hold until temperature is uniform throughout the section.
-Soak as required. Cool in furnace.
Heat to 950 °C - 1020 °C and hold until temperature is uniform throughout the section. Quench in oil or air cool. Temper immediately while still hand touch warm.
Hardening from 1020 °C - 1060 °C will give optimum corrosion resistance, but hardening upto 980 °C will give the best combination of corrosion resistance and mechanical properties.
Min – Max: Heat to 650 °C - 750 °C and hold until temperature is uniform throughout the section.
-Soak as required. Cool in air.
Tempering within the range 150 °C - 200 °C will give optimum corrosion resistance and maximum hardness - up to 54 HRC depending upon section size. Tempering however within the range 400 °C - 550 °C should be avoided due to temper brittleness, resulting in a considerable reduction in impact resistant properties and loss of corrosion resistance.
*Heating temperatures, rates of heating, cooling and soaking times will vary due to factors such as work piece size / shape, also furnace type employed, quenching medium and work piece transfer facilities etc.
420 is machine-able in both the hardened and tempered conditions such as drilling, turning and bending. But it is recommended that machining in hardened condition should be avoided.
420 is not generally recommended for welding in either the annealed or hardened and tempered conditions, due to its air hardening capability which can lead to the formation of brittleness, resulting in cold cracking due to contraction stresses within the weld and heat affected zones. The higher the carbon content, the higher the hardening capability and greater risk of cracking. But despite all this, it is still easy to weld as compared to 440C grade.
Pre heating and inter-pass temperature control during welding, plus very slow cooling and post-weld annealing is the best method to prevent cracking.
Chemical Composition ranges of 420 J2 stainless steel